This document specifies two calcination methods for the determination of the textile glass and mineral filler content of glass-reinforced plastics:
— Method A: for the determination of the textile glass content when no mineral fillers are present.
— Method B: for the determination of the textile-glass and mineral-filler content when both components are present.
This document is applicable to the following types of material:
— prepregs made from yarns, rovings, tapes or fabrics;
— SMC, BMC and DMC moulding compounds;
— textile-glass-reinforced thermoplastic moulding materials and granules;
— filled or unfilled textile-glass laminates made with thermosetting or thermoplastic resins.
The methods do not apply to the following types of reinforced plastic:
— those containing reinforcements other than textile glass;
— those containing materials which do not completely burn off at the test temperature (for example, those based on silicone resin);
— those containing mineral fillers which degrade at temperatures below the minimum calcination temperature.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2023-08Этап: Опубликование международного стандарта [60.60]
-
Версия: 3
-
Технический комитет :ISO/TC 61/SC 13ICS :83.120
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 1172:1996
-
Сейчас
-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00